Ultrason? S 3010
聚砜
產品說明:
Ultrason S 3010 is medium viscosity injection molding grade with improved toughness and chemical resistance (stress crack resistance).
Applications
Typical applications include laboratory accessories and household parts.
特性 | - Good ESCR (Stress Crack Resist.)、耐化學性良好、韌性良好、中等粘性
|
用途 | |
機構評級 | |
RoHS 合規性 | |
形式 | |
加工方法 | |
多點數據 | Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 | 1.23 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (360°C/10.0 kg) | 2.44 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.74 | % |
|
流量 | 0.70 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.80 | % |
|
平衡, 73°F, 50% RH | 0.30 | % |
|
球壓硬度 | 19600 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 370000 | psi | ISO 527-2 |
拉伸應力 (屈服, 73°F) | 10900 | psi | ISO 527-2 |
拉伸應變 (屈服, 73°F) | 6.0 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
| ISO 179 |
-22°F | 2.9 | ft·lb/in2 |
|
73°F | 2.6 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179 |
-22°F | 無斷裂 |
|
|
73°F | 無斷裂 |
|
|
懸壁梁缺口沖擊強度 |
|
| ISO 180 |
-22°F | 2.9 | ft·lb/in2 |
|
73°F | 2.6 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 351 | °F | ISO 75-2/A |
線形熱膨脹系數 - 流動 | 2.9E-5 | in/in/°F |
|
RTI Elec |
|
| UL 746 |
0.06 in | 311 | °F |
|
0.12 in | 311 | °F |
|
RTI Imp |
|
| UL 746 |
0.06 in | 266 | °F |
|
0.12 in | 266 | °F |
|
RTI |
|
| UL 746 |
0.06 in | 311 | °F |
|
0.12 in | 311 | °F |
|
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 940 | V/mil | IEC 60243-1 |
介電常數 |
|
| IEC 60250 |
100 Hz | 3.10 |
|
|
1 MHz | 3.10 |
|
|
耗散因數 |
|
| IEC 60250 |
100 Hz | 8.0E-4 |
|
|
1 MHz | 6.4E-3 |
|
|
漏電起痕指數 | 125 | V | IEC 60112 |
UL 阻燃等級 |
|
| UL 94 |
0.06 in | HB |
|
|
0.12 in | HB |
|
|
干燥溫度 | 266 到 302 | °F |
|
干燥時間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 644 到 734 | °F |
|
模具溫度 | 284 到 356 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|